Silver solder (Silfos 2) - bright L-Ag 2CuP, d = 2 mm, L = 500 mm This silver solder offers the highest quality and precision for your soldering applications in cooling, air conditioning and ventilation technology or heat pumps. With a composition of 91.5% copper, 2% silver and 6.5% phosphorus, it guarantees optimum results at various temperatures.Technical details: Composition (%): Cu - 91.5, Ag - 2, P - 6.5 Melting point: 645 - 825 °C Standards: EN 1044 CP 105, DIN 8513L-Ag2P, AWS 5.8 BCuP-6 Dimensions: d = 2 mm, L = 500 mm 1. perfect results: Achieve precise and durable joints in your projects with this high-quality silver solder. 2. versatile application: Ideal for use in refrigeration, air conditioning and ventilation technology as well as heat pumps - an indispensable tool for professionals.

German description follows - please contact us if you have any questions about the product.

Phosphorlot - blank L-Cu P7, d = 2.0 mm, L = 500 mm Phosphorus brazing rod L-Cu P7 is a high-quality welding rod that is used in refrigeration, air conditioning and ventilation technology as well as in heat pumps. With a composition of 93.2 - 92.5 % copper and 6.8 - 7.5 % phosphorus, this solder offers excellent welding quality and strength. Technical details: Melting point: 710 - 820 °C Density: 8.5 g/cm3 Tensile strength: 250 Mpa Standards: ISO 3677 B-Cu93P-710/890, EN 1044 CP 202, DIN 8513 L-CuP7, AWS 5.8 BCuP - 2 Sales-promoting content: The phosphorus solder L-Cu P7 is characterised by its high tensile strength and melting point, which ensures a reliable and durable welded joint. With one rod, you get a length of 500 mm and a weight of approx. 0.01 kg, which makes it easy to handle. The quality and reliability of this solder is guaranteed by the ISO 3677, EN 1044, DIN 8513 and AWS 5.8 standards, making it an ideal choice for professional applications in refrigeration, air conditioning and ventilation technology as well as heat pumps.

Copper sleeve i/i 10 mm, 5270 This copper sleeve i/i 10 mm from the 5270 family is ideal for use in cooling systems, air conditioning systems, ventilation technology and heat pumps. The high-quality workmanship in accordance with DIN EN 1254-1 ensures a reliable and durable connection.Technical details: Type designation: 5270 010000000 Short text: CU MUFFE 5270 10MM I/I Dimensions: 10 mm Available in the dimensions: 6mm - 108mm Application range: socket I/I Advantages and benefits: The copper sleeve i/i 10 mm scores with the following advantages: Reliable connection thanks to high-quality workmanship in accordance with DIN EN 1254-1 Easy installation and soldering Suitable for various applications in refrigeration, air conditioning and ventilation technology as well as heat pumps

Phosphorlot - brazing alloy L-CU P6, D = 2.0 mm, L = 500 mm The phosphor plumb bob L-CU P6 is ideal for use in the field of cooling, air conditioning and ventilation technology as well as for heat pumps. The rod has a diameter of 2.0 mm and a length of 500 mm. Technical details: Composition (%): Cu - 94.1 - 93.5, P - 5.9 - 6.5 Melting point: 710 - 890 °C Density: 8.1 g/cm3 Tensile strength: 250 Mpa Standards: ISO 3677 B-Cu94P-710/890, EN 1044 CP 203, DIN 8513 L-CuP6 Sales-promoting content: This phosphorus brazing alloy is characterised by its high tensile strength and melting point of 710 - 890 °C. It complies with the ISO 3677 B-Cu94P-710/890, EN 1044 CP 203 and DIN 8513 L-CuP6 standards, which emphasises its quality and reliability. With a density of 8.1 g/cm3, it is also particularly durable and resistant. 1 piece = 1 bar of approx. 0.1 kg

Phosphorlot - Brazing alloy L-CU P7SN The phosphorus brazing alloy L-CU P7SN is a high-quality brazing alloy with a diameter of 2.0 mm and a length of 500 mm. It consists of a special composition of Cu (copper) 87.1 - 85.3%, P (phosphorus) 6.4 - 7.2% and Sn (tin) 6.5 - 7.5%. With a melting point of 650 - 700 °C, it is ideal for various soldering applications in the field of refrigeration, air conditioning and ventilation technology as well as heat pumps.Technical details: Diameter: 2.0 mm Length: 500 mm Composition: Cu - 87.1 - 85.3%, P - 6.4 - 7.2%, Sn -6.5 - 7.5% Melting point: 650 - 700 °C Density: 8.0 g/cm3 Tensile strength: 250 Mpa Standards: ISO 3677 B-Cu86SnP-650/700, EN 1044 CP 302 Advantages and benefits: The phosphorus solder offers a high tensile strength of 250 Mpa, which ensures stable and reliable solder joints. With its precise composition and optimum melting point, it is ideal for professional soldering applications in refrigeration, air conditioning and ventilation technology as well as heat pumps. The ISO 3677 and EN 1044 standards guarantee the quality and reliability of this solder. Order a 0.1 kg bar of phosphorus solder now and benefit from the outstanding properties of this high-quality brazing alloy for your soldering projects.

Leak Lock 39 ml – plastic sealant for threads and sealing surfaces Product description Leak Lock is a high-quality, plastic sealant for sealing threaded joints, flanged joints, sealing surfaces and mating surfaces. The viscous, spreadable paste adheres to clean surfaces, fills small voids and, once the parts are joined, forms a chemically resistant, flexible and liquid-tight seal. The sealant is suitable for many applications in refrigeration, air conditioning and ventilation technology, in plant engineering, and for technical pipe and bolted joints. Leak Lock remains permanently elastic, does not become brittle and can be used even under vibrations, temperature fluctuations and in pressure and vacuum applications. Your benefits For sealing threads, flanges and sealing surfaces Remains flexible and does not become brittle Suitable for pressure and vacuum applications Wide temperature range from -129 °C to +204 °C Pressure-resistant up to approx. 690 bar Adheres to clean metal and plastic surfaces Resistant to many refrigerants, oils, water, gases and chemicals Helps prevent nuts, bolts, plugs and fittings from coming loose due to vibrations Handy 39 ml tube for servicing, assembly and workshop use Typical applications Leak Lock is used wherever threaded or sealing surfaces need to be sealed permanently and flexibly. This includes, amongst other things, screw connections, flange surfaces, gaskets, fittings, plugs, valves and contact surfaces between different materials. Leak Lock is particularly well known in the refrigeration and air-conditioning sectors as a sealing paste for selected service and installation work. For suitable connections, it can help to reduce moisture ingress into threaded areas and provide a flexible seal against refrigerants, oil or industrial gases. Suitable materials Leak Lock can be used on many clean metal and plastic surfaces. These include, amongst others, aluminium, aluminium alloys, cast iron, copper, copper alloys, brass, bronze, magnesium alloys, carbon steel, stainless steel, galvanised surfaces, PVC, CPVC, ABS, fibreglass, black polypropylene and Kynar. Application Thoroughly clean the sealing surfaces and remove any dust, oil and grease. Apply Leak Lock to both contact surfaces using a brush, spatula or suitable applicator. Allow to flash off briefly to allow initial adhesion to develop. Assemble the joint and tighten to the correct torque. Observe the curing or load-bearing time, which depends on the pipe size, material and ambient temperature. Important notes Leak Lock is not recommended for use with alcohols. Alcohol-based cleaners may be used for pre-cleaning, but must be allowed to evaporate completely before application. For unwanted contamination, a suitable cleaning agent may be used in accordance with the manufacturer’s instructions. Leak Lock should not be applied indiscriminately to every joint. It is not recommended for use on pre-charged quick-connect refrigeration lines in air-conditioning systems. The decisive factors are always the type of joint, the manufacturer’s specifications and the specific application. Why Leak Lock? Why Leak Lock? Leak Lock is a practical solution when a sealant that remains flexible is required for threads, flanges and sealing surfaces. Thanks to its high chemical resistance, wide temperature range and suitability for vacuum and pressure applications, the paste is particularly well-suited for use in the assembly, servicing and repair of technical systems. Leak Lock 39 ml is a plastic thread sealant for refrigeration, air-conditioning, ventilation and industrial applications. This flexible sealing paste is suitable for many metals and plastics, is resistant to numerous refrigerants, oils, water and technical gases, and can be used for threaded connections, flange surfaces, sealing surfaces and mating surfaces. Technical data Product Leak Lock Product type Thread sealant / sealing paste Contents 39 ml Consistency Flowable paste Colour Light blue Solvents Ethanol and isopropanol Temperature range -129 °C to +204 °C Pressure range High vacuum to 10,000 psi / approx. 690 bar VOC content in use 340.8 g/l After curing 0 VOC according to the manufacturer’s specifications Shelf life Unlimited when stored in a tightly sealed container Suitable for Threaded connections Flange connections Sealing surfaces Mating surfaces Fittings and plugs Metal and plastic joints Connections subject to vibration Media resistance Refrigerants, including many CFCs, HFCs, HCFCs and PFCs Refrigeration oils, mineral oils, POE, PVE and alkylbenzene oils Water and seawater Air and industrial gases Natural gas, LPG, propane, butane and isobutane Petrol, diesel, kerosene and other fuels Many solvents and diluted acids Curing time / load-bearing capacity 0 to 1/2" approx. 1–2 hours 1/2" to 1 1/2" approx. 4–6 hours 2" to 4" Overnight The actual curing time depends on the pipe size, the amount applied and the ambient temperature.

German description follows - please contact us if you have any questions about the product.